Experiments show that :

When the DCP ≥ 0.6: product surface cracking, wrinkled ; DCP <0.6: better visual surface of the article ; the above results are analyzed : the experimental conditions , when the DCP is greater than or equal to 0.6, the cross linking rate too large , then the AC had a chance to fully decompose , EVA FOAM MANUFACTURER melt viscosity has been great , the bubble does not fully inflate , so the bubble pressure in vivo large ( the force is temporary equilibrium ) , but the pressure does not destroy EVA FOAM MANUFACTURER cross linking system , when unload the outside pressure, cracks , wrinkles . From theorized that : when the amount of less than a certain value, DCP , this value corresponds to the amount of a gel , and this gel is to get a good amount of the minimum of foam ( about 65% ) .

Vinyl acetate copolymer (EVA FOAM MANUFACTURER) cross-linked EVA foam manufacturer material has two formulations of low density, good physical properties , weather resistance, non-toxic , etc. , in recent years the development of ten 2. 1 EVA FOAM MANUFACTURER

Points quickly , widely used in sports equipment, mattresses, children's floor , life-saving system EVA FOAM MANUFACTURER is non-polar , crystalline ethylene monomer and a polar , non- product , high-end athletic shoes and other manufacturers . However, the crosslinked EVA FOAM MANUFACTURER EVA foam manufacturer crystalline elastic material vinyl acetate monomer by high pressure polymerization of a thermoplastic body , tear resistance and peel resistance , etc. is not good enough , thus limiting its enable resin , Since the introduction of the molecular chain vinyl acetate monomer , with the knot .